Thermo-Mechanical Behaviour of Flax-Fibre Reinforced Epoxy Laminates for Industrial Applications
2015
The present work describes the experimental mechanical characterisation of a natural flax fibre reinforced epoxy polymer composite. A commercial plain woven quasi-unidirectional flax fabric with spun-twisted yarns is employed in particular, as well as unidirectional composite panels manufactured with three techniques: hand-lay-up, vacuum bagging and resin infusion. The stiffness and strength behaviours are investigated under both monotonic and low-cycle fatigue loadings. The analysed material has, in particular, shown a typical bilinear behaviour under pure traction, with a knee yield point occurring at a rather low stress value, after which the material tensile stiffness is significantly r…
On relation between J-integral and heat energy dissipation at the crack tip in stainless steel specimens
2019
In this paper, an experimental procedure to evaluate the elastic-plastic J-integral at the tip of a fatigue crack is presented. According to this new approach, the elastic component of the J-integral is derived from Thermoelastic Stress Analysis, while the plastic component of the J-integral is derived from the heat energy loss. An analytical link is proposed to apply this new experimental technique. Therefore, the elastic-plastic J-integral range was evaluated starting from infrared temperature maps measured in situ during crack propagation tests of AISI 304L stainless steel specimens. It was found that the range of the infrared thermography-based J-integral correlated well the crack growt…
Investigation on the influence of the surface resin rich layer on the thermoelastic signal from different composite laminate lay-ups
2006
This work presents a set of experimental results based on the measured thermoelastic signal from GRP composite coupons adopting different lay-ups. A comparison is made with the thermoelastic signal predicted by two different analytical models: one based on the classical law of the thermoelastic effect for orthotropic materials, and the other based on a novel theory accounting for the presence of a resin layer on the external surface of the composite structure. The composite coupons were designed such to determine a significant difference in the predictions made by the two theoretical models. Experimental results have shown a far better match with the predictions based on the novel theory ac…
Lock-In Signal Post-Processing Techniques in Infra-Red Thermography for Materials Structural Evaluation
2013
This paper describes the potential of off-line thermographic signal processing by means of Lock-In Correlation algorithms, in order to implement structural health monitoring and stress analysis techniques. Thermal datasets acquired by infrared thermocameras are locked-in and correlated numerically with opportune reference signals, and amplitude and phase values of various harmonics retrieved by means of a Fast Fourier Transform and time averaging based filtering. This information is then processed for NDT defect probing and for evaluating the Thermoelastic Effect induced temperature changes. Two case studies in particular are discussed, implementing the proposed signal lock-in processing: a…
A quantitative investigation on the thermoelastic effect of CFRP laminates
2009
The thermoelastic effect on CFRP laminates with various lay-ups is investigated. A thick low crimp unidirectional fabric reinforcement is adopted. The measured thermoelastic signal is compared with predictions from two analytical models based on the meso-mechanical bulk properties of the lamina and on assuming a strain witness behaviour of the surface resin rich layer.
ANALISI E SVILUPPO DI UN SETUP SPERIMENTALE PER LA DETERMINAZIONE DELLA TENACITÀ A FRATTURA A MODO II NEI MATERIALI COMPOSITI E IBRIDI
Il presente lavoro di Tesi si propone a compimento del percorso previsto dal Ciclo XXVI del corso di Dottorato di Ricerca in Ingegneria Civile e Ambientale – Indirizzo Materiali – seguito durante il triennio Gennaio 2013- Dicembre 2015 presso l’Università degli Studi di Palermo. L’elaborato si sviluppa in due principali sezioni. Dopo un’introduzione all’argomento affrontato, nella prima parte del lavoro, viene analizzato, sia sperimentalmente che numericamente, un setup tipicamente utilizzato nell’industria aeronautica per la caratterizzazione delle delaminazione a MODO II nei materiali compositi (Transverse Crack Tensile test – TCT-test). A partire dai risultati ottenuti dalle analisi prel…
A Quantitative Analysis of the Thermoelastic Effect in CFRP Composite Materials
2010
In this study the thermoelastic signal from carbon fibre-reinforced plastic (CFRP) laminates is investigated. A comparison between the theoretical and experimental values of the thermoelastic signal is reported, with the theoretical predictions obtained from two different quantitative models. These models are based on the classic thermoelastic effect law extended to the case of orthotropic materials (by using the mesomechanical or bulk approach), and the modified law assuming that the surface resin-rich layer behaves as a strain witness of the laminate. It is found that the theoretical predictions of the two models can be strongly and differently influenced by the intrinsic orthotropy of ca…
Infrared thermography-based evaluation of the elastic-plastic J-integral to correlate fatigue crack growth data of a stainless steel
2019
Abstract The elastic-plastic J-integral is adopted to correlate fatigue crack growth data of ductile metals. An analytical link is known to exist between the J-integral and the strain energy density averaged in a control volume embracing the crack tip. On the other hand, the strain energy fluctuation is the source of temperature variations close to a fatigue crack tip of a metal material; hence the possibility to measure the J-integral from infrared thermographic scanning at the crack tip is envisaged and it is the focus of this paper. It is proposed that the elastic component of the J-integral is derived from a thermoelastic stress analysis, while the plastic component of the J-integral is…
Experimental evaluation of through-the-thickness stress distribution in transverse crack tension test samples
2015
Transverse Crack Tension (TCT) samples represent an alternative to End Notched Flexure configurations for the characterization of pure mode II fracture toughness of Fibre Reinforced Polymer composites. TCT is supposed to reproduce a pure Mode II failure mechanism while avoiding the frictional energy dissipation between the flanks of a starter crack. The TCT geometry is that of a unidirectional tensile sample where a number of embedded plies, centered on the middle plane, are cut in the transverse fibres direction. The tensile loading should then activate four symmetric fronts of mode II delamination from the transverse cut tips. The present work describes the implementation of two full fiel…
Investigation of the Thermomechanical Response of Cyclically Loaded NiTi Alloys by Means of Temperature Frequency Domain Analyses
2021
Nickel–Titanium (NiTi) shape memory alloys subjected to cyclic loading exhibit reversible temperature changes whose modulation is correlated with the applied load. This reveals the presence of reversible thermomechanical heat sources activated by the applied stresses. One such source is the elastocaloric effect, accounting for the latent heat of Austenite–Martensite phase transformation. It is, however, observed that when the amplitude of cyclic loads is not sufficient to activate or further propagate this phase transformation, the material still exhibits a strong cyclic temperature modulation. The present work investigates the thermomechanical behaviour of NiTi under such low-amplitude cyc…